Model No.: XCPU-E836
Jenama: Xuchuan Chemical
Tempat Asal: China
Jenis: Resin Sintetik Dan Plastik
Application: Rollers
CPU untuk elastomer
Penerangan Produk
Polyester Prepolymer XCPU-E836
Prepolimer polyseter untuk cincin
1. Produk ini adalah poliester poliol dan toluene diisocyanate (T-80) dalam sintesis prepolimer poliuretana poliester
2. Ciri -ciri: Rintangan haus yang sangat baik, rintangan minyak, sifat mekanikal
3. Kegunaan: Saring, bahagian jentera, cincin pengedap, roller PU dan produk lain
Polyether Polyurethane Prepolymer
Name of products
|
Appearances
|
Viscosity(mPa.s/85℃)
|
NCO% content
|
Package(kg)
|
XCPU-E836
|
solid
|
2000-2200
|
3.60-3.80
|
20 / 200
|
5、Mixing and Curing Conditions
|
|
|
|
|
|
|
||||||
MOCA Level
|
Recommended % Theory
|
Prepolymer Temperature
|
Curative Temperature
|
Pot Life
|
Demould Time
|
Post Cure Time
|
||||||
%
|
%
|
℃
|
℃
|
mins
|
@ 100°C (hrs)
|
@ 100°C (hrs)
|
||||||
10.8
|
95
|
75-85
|
110-120
|
4-4.5
|
1
|
10
|
Hardness
|
Shore A
|
86
|
Tensile Strength
|
MPa
|
49
|
100% Modulus
|
MPa
|
5.2
|
300% Modulus
|
MPa
|
9.7
|
Angle Tear Strength, Die C
|
kN/m
|
88
|
Trouser Tear Strength
|
kN/m
|
38
|
Elongation
|
%
|
680
|
Resilience
|
%
|
44
|
DIN Abrasion Resistance 10N
|
mm 3
|
44
|
Cured Specific Gravity
|
g/cm3
|
1.26
|
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.