Model No.: XC-9080W/XC-6088W
Jenama: Xuchuan Chemical
Tempat Asal: China
Application: Outsole, slippers, wedge shoes
Code: XC-9080W/XC-6088W
Keywords: water soluble polyurethane resin
Appearance: Liquid
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line
Unit Jualan | : | Kilogram |
Jenis Pakej | : | 20 & 225 kg/gendang |
Contoh Gambar | : |
Application | shoe sole |
Keywords | water soluble polyurethane resin |
A/B Materials Temperatures(℃) | A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) | 100/100~102 |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 30~40 |
Free Rise Foam Density(g/cm3) | 0.21~0.26 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | Demold Time(min) |
Molded Density (g/cm3) | 0.35~0.60 |
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line |
|||||||
Application: Outsole, slippers, wedge shoes |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-9080W |
Cream,White,liquid |
1000~1300 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-6088 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
Materials preheat |
|||||||
A-9080W: preheated at 50~60℃ for 6~8 hours. |
|||||||
B-6088: preheated at 50~60℃ for 6~8 hours. |
|||||||
Typical processing parameters & Reaction parameter. |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/100~102 |
6~8 |
30~40 |
0.21~0.26 |
45~55 |
5~7 |
The adding content of C-2 should be 210g±10g/18kg. |
|||||||
The adding content of water should be 0~80g/18kg according to the reality. |
|||||||
The adding content of hardener should be 0~1200g/18kg according to the reality. |
|||||||
Physical propertiesShoe Sole Pu Chemical |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
Williams abrasion |
/ |
Physical properties |
0.35~0.60 |
60~88 |
4~7 |
200~300 |
11~20 |
130~200 |
/ |
Demold time may be prolonged with the increase of sole thickness. |
|||||||
|
|||||||
|
Data fizikal ini diperoleh dengan menguji sampel tebal 6mm.
Data yang disenaraikan di atas hanya untuk rujukan. Data terperinci tertakluk kepada pengeluaran praktikal. Jika permintaan lain untuk sifat fizikal, sila hubungi kami.
Sistem PU untuk kasut tunggal, pelekat untuk kasut, CPU, TPU, poliester poliol, resin PU untuk dakwat, pelekat cair panas PUR, pelekat untuk pakej fleksibel, resin PU untuk kulit sintetik
Xuchuan Chemical yang ditubuhkan pada tahun 2007, modal berdaftar syarikat adalah RMB 500 juta. Produk utama adalah semua polies poliol, resin poliuretana untuk kasut, resin poliuretana berasaskan air dan pelarut untuk kulit buatan, pelekat ikatan poliuretana dan pelekat cair panas poliuretana.
Sekarang Xuchuan mempunyai 4 pangkalan pengeluaran moden, kapasiti pengeluaran mencapai 630,000 tan setahun, produk yang dieksport ke 32 negara dan wilayah di dunia.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.