Model No.: A-9080W/B-6088
Jenama: Xuchuan
Tempat Asal: China
Jenis: Resin Sintetik Dan Plastik
Appearence: liquid
Keywords: Lady shoe sole
Characteristic: Low density and high hardness
Model Number: A-9080W/B-6088
Other Names: PU Resin
Brand Name: Xuchuan
Application: shoe sole
Unit Jualan | : | Kilogram |
Jenis Pakej | : | Polyol: 210 & 18kg/drum isosianat: 225 & 20kg/drum tambahan: 20kg/gendang |
Contoh Gambar | : |
PENERANGAN PRODUK
Bahan mentah poliuretana
Kertas insole papan bahan cecair busa penebat poliol dan isosianat poliuretana acrylate resin untuk kasut tunggal
Application | shoe sole |
Keywords | Lady shoe sole |
A/B Materials Temperatures(℃) | A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) | 100/100~102 |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 30~40 |
Free Rise Foam Density(g/cm3) | 0.21~0.26 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | Demold Time(min) |
Molded Density (g/cm3) | 0.35~0.60 |
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line |
|||||||
Application: Outsole, slippers, wedge shoes |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-9080W |
Cream,White,liquid |
1000~1300 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-6088 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
|
|||||||
A-9080W: preheated at 50~60℃ for 6~8 hours. |
|||||||
B-6088: preheated at 50~60℃ for 6~8 hours. |
|||||||
Typical processing parameters & Reaction parameter. |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/100~102 |
6~8 |
30~40 |
0.21~0.26 |
45~55 |
5~7 |
The adding content of C-2 should be 210g±10g/18kg. |
|||||||
The adding content of water should be 0~80g/18kg according to the reality. |
|||||||
The adding content of hardener should be 0~1200g/18kg according to the reality. |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
Williams abrasion |
/ |
Physical properties |
0.35~0.60 |
60~88 |
4~7 |
200~300 |
11~20 |
130~200 |
/ |
Demold time may be prolonged with the increase of sole thickness. |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Xuchuan Chemical yang ditubuhkan pada tahun 2007, modal berdaftar syarikat adalah RMB 500 juta. Produk utama adalah semua polies poliol, resin poliuretana untuk kasut, resin poliuretana berasaskan air dan pelarut untuk kulit buatan, pelekat ikatan poliuretana dan pelekat cair panas poliuretana.
Sekarang Xuchuan mempunyai 4 pangkalan pengeluaran moden, kapasiti pengeluaran mencapai 630,000 tan setahun, produk yang dieksport ke 32 negara dan wilayah di dunia.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.