liquid
Cream Time (s):8-10
End of Rise Time (s):60-70
Demold Time(min):5-7

Hubungi sekarang

Penerangan produk

Atribut Produk

Pembungkusan & Penghantaran

Penerangan produk

Atribut Produk

Model No.: XC-3070,XC-8280

Jenama: Xuchuan Chemical

Tempat Asal: China

Jenis: Resin Sintetik Dan Plastik

Brand Name: Xuchuan

Appearence: liquid

Model Number: XC-3070,XC-8280

Application: Industrial tyre wheel

Product Name: Polyurethane

Characteristic: Good handle, smooth surface

Package(kg): 18/20 kg

Pembungkusan & Penghantaran

Unit Jualan	:	Ton
Jenis Pakej	:	220kg/gendang
Contoh Gambar	:

pelekat untuk kasut



Penerangan produk

Penerangan Produk Kimia Roda PU

Pu resin kasut sandal bahan mentah tunggal Jenis buih poliuretana untuk membuat tayar buih

Perincian produk resin pemutus poliuretana roda

Application	Industrial tyre wheel
Product name	Polyurethane
A/B Materials Temperatures(℃)	40~45/38~42
A+C/B Mix ratio (By weight)	100/101~103
Cream Time (s)	8~10
End of Rise Time (s)	60~70
Free Rise Foam Density(g/cm3)	0.24~0.26
Mold Temperature(℃)	45~55
Demold Time(min)	5~7

Characteristic: Good handle, smooth surface
Application: Tire
Typical properties of PU matrix
Name of products	Appearance	Viscosity (mPa·s/40℃)	Density (g·cm^-3/40℃)	Package(kg)	/
A-3070	Liquid	1000~1400	1.01~1.02	18
B-8280	Yellowish transparent liquid or waxy	800~1200	1.08~1.2	20
Materials preheat
A-3070: preheated at 50~60℃ for 6~8 hours.
B-8280: preheated at 50~60℃ for 10~12 hours.
Typical processing parameters & Reaction parameter
Items	A/B Materials Temperatures(℃)	A+C/B Mix ratio (By weight)	Cream Time (s)	End of Rise Time (s)	Free Rise Foam Density(g/cm³)	Mold Temperature(℃)	Demold Time(min)

Parameter	40~45/38~42	100/101~103	8~10	60~70	0.24~0.26	45~55	5~7
The adding content of C-2 should be 250g±10g/18kg
The adding content of water should be 0~90g/18kg according to the reality
The adding content of hardener should be 0~600g/18kg according to the reality
Physical properties
Items	Molded Density (g/cm3)	Hardness (Shore A )	Tensile strength (MPa)	Elongation (%)	Tear Strength (kN/m)

Physical properties	0.50~0.70	55~68	7.5~9.0	340~450	24~33
Demold time may be prolonged with the increase of sole thickness.
These physical data are acquired by testing a sample of 6mm thick.
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.

Gambaran Keseluruhan Syarikat

company company

Xuchuan Chemical yang ditubuhkan pada tahun 2007, modal berdaftar syarikat adalah RMB 500 juta. Produk utama adalah semua polies poliol, resin poliuretana untuk kasut, resin poliuretana berasaskan air dan pelarut untuk kulit buatan, pelekat ikatan poliuretana dan pelekat cair panas poliuretana.

Sekarang Xuchuan mempunyai 4 pangkalan pengeluaran moden, kapasiti pengeluaran mencapai 630,000 tan setahun, produk yang dieksport ke 32 negara dan wilayah di dunia.

Bengkel